Enhanced Pinning in a Broad Angular Range by 1D-APCs With a Coherent Interface

One-dimensional artificial pinning centers (1D-APCs) in YBa2Cu3O7-x nanocomposite films provide strong collective pinning at magnetic field B//c-axis. In this work, we reveal a 1D-APC/YBa2Cu3O7-x interface is preferred for high pinning efficiency of individual 1D-APCs including BaHfO3 and BaZrO3. The coherent 1D-APC/YBa2Cu3O7-x interface may be obtained via either growth of the nanocomposite films at optimal condition or Ca-diffusion to dynamically reduce the interface strain during the nanocomposite film growth. Interestingly, the high pinning efficiency of the 1D-APCs with coherent interfaces with YBCO not only lead to a high critical current density (Jc) in magnetic fields up to 9.0 T at H//c-axis but also enhanced Jc over a larger angular range when H is away from H//c-axis up to θ = 60-80 degree than that in the case the interface is defective. This result suggests the importance of understanding and engineering the APC/YBCO interface for optimal pinning in nanocomposite films.