Light ion irradiation effects on stuffed Lu₂(Ti _2-xLu_x)O_7-x/2 (x = 0, 0.4 and 0.67) structures

We have recently synthesized "stuffed" (i.e., excess Lu) Lu ₂(Ti_2-xLu_x)O_{7- x/2} (x = 0, 0.4 and 0.67) compounds using conventional ceramic processing. X-ray diffraction measurements indicate that stuffing more Lu³⁺ cations into the oxide structure leads eventually to an order-to-disorder (O-D) transition, from an ordered pyrochlore to a disordered fluorite crystal structure. At the maximum deviation in stoichiometry (x = 0.67), the Lu³⁺ and Ti⁴⁺ ions become completely randomized on the cation sublattices, and the oxygen "vacancies" are randomized on the anion sublattice. Samples were irradiated with 400 keV Ne²⁺ ions to fluences ranging from 1 × 10¹⁵ to 1 × 10 ¹⁶ ions/cm² at cryogenic temperatures (∼77 K). Ion irradiation effects in these samples were examined by using grazing incident X-ray diffraction. The results show that the ion irradiation tolerance increases with disordering extent in the non-stoichiometric Lu₂(Ti _2-xLu_x)O_{7-x /2}.