Reinforcement shape effects on the fracture behavior and ductility of particulate-reinforced 6061-Al matrix composites

Particle shape effects on the fracture and ductility of a spherical and an angular particulate-reinforced 6061-A1 composite containing 20 pet vol Al₂O₃ were studied using scanning electron microscopy (SEM) fractography and modeled using the finite element method (FEM). The spherical particulate composite exhibited a slightly lower yield strength and work hardening rate but a considerably higher ductility than the angular counterpart. The SEM fractographic examination showed that during tensile deformation, the spherical composite failed through void nucleation and linking in the matrix near the reinforcement/matrix interface, whereas the angular composite failed through particle fracture and matrix ligament rupture. The FEM results indicate that the distinction between the failure modes for these two composites can be attributed to the differences in the development of internal stresses and strains within the composites due to particle shape.